- Nilit FRIANYL B63 GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
Nilit FRIANYL B63 GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 GV15 Nylon 6 for injection molding, 15% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 - 2.6 % | 1.6 - 2.6 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0070 - 0.014 cm/cm | 0.0070 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 155 MPa | 22500 psi | ISO 2039-1 |
| Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 5.50 GPa | 798 ksi | ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 4.40 GPa | 638 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 3.50 J/cm² @Temperature -40.0 °C |
16.7 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| 0.800 J/cm² | 3.81 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 575 V | 575 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- PolyChem Alloy FilmStat 3K2
- Dielectric Polymers NT-711 Electrical/Mechanical Tape (discontinued **)
- Kazanorgsintez Carbanox SKD-10 Polyethyleneglycol Mixture
- Intercontinental Polymers 1128 Bicomponent PBT/PET Fiber Type - 1.8 Denier X 3 Inches
- SPS Guang Zhou POLLITEâ„¢ 1002G30 Flame-retarded/GF30%-Polycarbonate
- Shuman 980 Grey Polycarbonate
- Techmer ES HiFill® PPSU A1 0200 B LE
- 3M Diamond Grade™ 983 Conspicuity Markings
- 3M Dyneon™ TF 5050Z PTFE
Copyright © lookpolymers.com All Rights Reserved