- Nilit FRIANYL A63 W-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
Nilit FRIANYL A63 W-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 W-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.4 % | 1.4 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 7.0 % | 5.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.016 cm/cm | 0.0080 - 0.016 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength at Break | 144 MPa | 20900 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.40 J/cm² | 16.2 ft-lb/in² | DIN 53453 |
| 2.90 J/cm² @Temperature -40.0 °C |
13.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.750 J/cm² | 3.57 ft-lb/in² | DIN 53453 |
| 0.650 J/cm² @Temperature -40.0 °C |
3.09 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 20 HI PA66, 20% glass beads
- SABIC Innovative Plastics Cycolac® BDT6500 ABS
- Kolon KOPA® KN3322VO Flame Retardant Nylon 66
- LG Chemical LUPOY GN5001RFH PC/ABS, Halogen Free Flame Retardant, Heat Resistance
- Indium Corp. Indalloy® 183 Au-Ge Solder Alloy
- Tisan TISETILEN® Flame Retardant (V0) Polyethylene
- Wellman Wellamid® MR340 42H-NBK1 Nylon 6, 34% Mineral Reinforced
- A. Schulman INVISION™ VX-5085UI Soft Touch Polyolefin Thermoplastic
- Universal Wire Works BAg-19 (AMS 4767) Silver Brazing Filler Metal
- Arkema Group Evatane® 1040 VN 4 Ethylene Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved