Bulk Molding Compounds BMC 200 Thermoset Polyester, Electrical Grade

Category	Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC
Manufacturer	BMC - Bulk Molding Compounds Inc.
Trade Name	BMC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bulk Molding Compounds BMC 200 Thermoset Polyester, Electrical Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BMC 200 is a high strength, low shrink molding compound. It can be supplied in bulk or extruded in pre-weighted slugs.Typical applications are circuit breakers, insulators, bobbins, electrical connectors and power tool housings.

Physical Properties	Metric	English	Comments
Specific Gravity	1.85 - 1.95 g/cc	1.85 - 1.95 g/cc
Water Absorption	0.15 - 0.25 %	0.15 - 0.25 %	24 hours, 23°C
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in

Mechanical Properties	Metric	English
Hardness, Barcol	40 - 50	40 - 50
Tensile Strength, Ultimate	27.6 - 41.4 MPa	4000 - 6000 psi
Flexural Strength	68.9 - 103 MPa	10000 - 15000 psi
Flexural Modulus	12.4 - 13.8 GPa	1800 - 2000 ksi
Compressive Strength	124 - 138 MPa	18000 - 20000 psi
Izod Impact, Notched	1.07 - 2.14 J/cm	2.00 - 4.00 ft-lb/in

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	>= 260 °C	>= 500 °F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Strength	13.8 - 14.6 kV/mm	350 - 370 kV/in	Step by Step
	14.6 - 16.5 kV/mm	370 - 420 kV/in	Short Time
Arc Resistance	>= 180 sec	>= 180 sec
Comparative Tracking Index	>= 500 V	>= 500 V

Processing Properties	Metric	English	Comments
Mold Temperature	138 - 166 °C	280 - 330 °F

Users viewing this material also viewed the following: