NatureWorks® Ingeo™ 6400D Fiber Grade PLA
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | NatureWorks LLC |
| Trade Name | Ingeo™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NatureWorks® Ingeo™ 6400D Fiber Grade PLA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NatureWorks® PLA polymer 6400D is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6400D is designed for extrusion into mechanically drawn continuous filament using conventional fiber spinning and drawing equipment. 6400D is typically well suited for fiber that is processed into bulk continuous filament (BCF), which is typically used in the manufacturing of carpet. NatureWorks® PLA 6400D can be converted into BCF using a one step spin-draw process.Applications: Bulk continuous filament; Tufted carpet – loop pile; Tufted carpet – cut pile; Broad loom carpet; Carpet mats
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Melt Density | 1.08 g/cc @Temperature 230 °C |
0.0390 lb/in³ @Temperature 446 °F |
ASTM D1238 |
| Viscosity Measurement | 4.0 | 4.0 | Relative Viscosity; CD Internal Viscotek Method |
| Melt Flow | 4.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 210 °C |
4.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | 35 - 45 % | 35 - 45 % | Fiber; ASTM D2256/ASTM D3822 |
| Tenacity | 0.177 - 0.212 N/tex | 2.00 - 2.40 g/denier | ASTM D2256/ASTM D3822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 - 170 °C | 320 - 338 °F | ASTM D3418 |
| Glass Transition Temp, Tg | 55.0 - 60.0 °C | 131 - 140 °F | ASTM D3417 |
| Shrinkage | 15 - 20 % | 15 - 20 % | Boiling Water, Bulk heat set; ASTM D2102 |
| 25 - 35 % | 25 - 35 % | Boiling Water, Bulk non-heat set; ASTM D2102 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Dew Point | -35.0 °C | -31.0 °F | |
| Drying Air Flow Rate | >= 14.2 l/min | >= 0.500 ft³/min (CFM) |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2865 TPE, PP Overmold or Standalone use
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic
- Covestro Bayblend® FR 3021 Polycarbonate + ABS, Mineral Filled
- Denka MALECCA K-200 ABS
- Ensinger TECAPEI® 30% Glass Reinforced, made from Ultem® 2300 PEI
- Dow Tyrin® CM0136 Chlorinated Polyethylene Elastomer
- Fainplast Compounds KL 90/4 Flexible PVC, Insulation for High Temperatures Lead Free
- BASF Elastollan® 1185A10X Wire & Cable Grade Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved