- A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene
A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyflam® RPP 1360 is a UL 94 V0 rated, non-halogenated homopolymer polypropylene flame retardant compound. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| UL RTI, Electrical | 105 °C @Thickness 0.780 mm |
221 °F @Thickness 0.0307 in |
UL 94 |
| Flammability, UL94 | V-0 @Thickness 0.780 mm |
V-0 @Thickness 0.0307 in |
|
| V-0 @Thickness 1.57 mm |
V-0 @Thickness 0.0618 in |
||
| V-0 @Thickness 3.05 mm |
V-0 @Thickness 0.120 in |
Users viewing this material also viewed the following:
- Nye Lubricants 174A (SO) Synthetic Oil
- SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER (Asia Pacific)
- Kolon KOPET® KP133G15BL G/F Reinforced Polyester Compound Resin (PET)
- Ineos ABS Lustran® LGM
- LG Chemical TR557 MABS, High Transparency, High Impact
- SABIC Innovative Plastics NORYL GTX GTX954 PPE+PA (Europe-Africa-Middle East)
- SCG Chemicals EL-Leneâ„¢ L2009F Linear Low Density Polyethylene Film
- Master Bond Supreme 10HTFS Silver Conductive Microelectronic Epoxy
- DuPont™ Kapton® 100ZT Polyimide Film, 25 Micron Thickness
- Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved