Stellar Canada CERAMITE® BCR Wear Resistant Castable

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Stellar Canada
Trade Name CERAMITE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Stellar Canada CERAMITE® BCR Wear Resistant Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ceramite is a family of wear resistant castables with a unique combination of high wear resistance, thermal resistance and mechanical strength. Ceramite is produced and supplied to end users world wide, both as mortars and as various precast components. Ceramite can easily be mixed, cast and shaped in any size and is thus comfortably to work with in-situ. Ceramite can be used in within a wide range of temperatures and applications exposed to thermal shock conditions in industries like for example aluminum, cement and ferro.Applications: Floor Tile, Hearth/Furnace Tile, Furnace Sills & Doors, Lintels, Pipe and Duct Linings, Feed Tubes, Troughs/Launders, Ladles, Dampers, Nozzle Blasters, Crucible Linings, Vortex, Burner Tip Cooler Plates, Nose Ring, Electrical Insulation, Cold Wear AreasSpecific Notes on This Grade: A castable with the combination of properties of BKR and CSR. Used in all industries where good abrasion and thermo shock properties are required. References as segments of aluminum furnaces, valves, impact/wear plates, launders etc…Information provided by Stellar Canada.
Physical Properties Metric English Comments
Bulk Density 2.74 g/cc
0.0990 lb/in³
As Placed
Porosity 14.9 %
14.9 %
Apparent
Mechanical Properties Metric English Comments
Modulus of Rupture 0.01300 GPa
1.886 ksi
Hot, prefired at 1832°F/24 hours (1000°C)
Flexural Strength 7.963 MPa

@Temperature 1200 °C
1155 psi

@Temperature 2192 °F
after Firing; ASTM-349
8.798 MPa

@Temperature 1000 °C
1276 psi

@Temperature 1832 °F
after Firing; ASTM-349
11.00 MPa

@Temperature 850.0 °C
1595 psi

@Temperature 1562 °F
after Firing; ASTM-349
16.40 MPa

@Temperature 500 °C
2379 psi

@Temperature 932 °F
after Firing; ASTM-349
Compressive Strength 116.00 MPa
16825 psi
Cold Crushing after 1560°F
98.002 MPa

@Temperature 1200 °C
14214 psi

@Temperature 2190 °F
after Firing; ASTM C-349
130.00 MPa

@Temperature 850 °C
18855 psi

@Temperature 1560 °F
after Firing; ASTM C-349
132.00 MPa

@Temperature 1000 °C
19145 psi

@Temperature 1830 °F
after Firing; ASTM C-349
195.00 MPa

@Temperature 20.0 °C
28283 psi

@Temperature 68.0 °F
after 7 days
199.00 MPa

@Temperature 500 °C
28863 psi

@Temperature 932 °F
after Firing; ASTM C-349
Thermal Properties Metric English Comments
Thermal Conductivity 2.528 W/m-K

@Temperature 600.0 °C
17.54 BTU-in/hr-ft²-°F

@Temperature 1112 °F
2.687 W/m-K

@Temperature 300 °C
18.65 BTU-in/hr-ft²-°F

@Temperature 572 °F
Maximum Service Temperature, Air 999 °C
1830 °F
Component Elements Properties Metric English Comments
Al2O3 63 %
63 %
CaO 6.3 %
6.3 %
Fe2O3 0.82 %
0.82 %
K2O 0.12 %
0.12 %
MgO 0.070 %
0.070 %
Na2O 0.060 %
0.060 %
SiC 17 %
17 %
SiO2 10 %
10 %
TiO2 2.0 %
2.0 %
Descriptive Properties Value Comments
Application Prefired
Precast Shapes