NOVA Chemicals Sclair® 11F2 Butene LLDPE Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Sclair® 11F2 Butene LLDPE Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Film Properties. Features: Low gel, high clarity, good seal characteristics.Applications: Liquid packaging, specialty blending, general purpose sealant.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.920 g/cc	0.0332 lb/in³	ASTM D792
Melt Flow	0.72 g/10 min @Load 2.16 kg, Temperature 190 °C	0.72 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.0 MPa	1600 psi	ASTM D882
Film Elongation at Break, MD	800 %	800 %	ASTM D882
Film Elongation at Break, TD	800 %	800 %	ASTM D882
Secant Modulus, MD	0.220 GPa	31.9 ksi	ASTM D882
Secant Modulus, TD	0.240 GPa	34.8 ksi	ASTM D882
Coefficient of Friction	0.40	0.40	ASTM D1894
Elmendorf Tear Strength, MD	2.00 g/micron	50.8 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	22.0 g/micron	559 g/mil	ASTM D1922
Dart Drop	3.00 g/micron	76.2 g/mil	F 50; ASTM D1709/A
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Film Tensile Strength at Break, TD	31.0 MPa	4500 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Vicat Softening Point	98.0 °C	208 °F	ASTM D1525
Brittleness Temperature	<= -68.0 °C	<= -90.4 °F	ASTM D696

Optical Properties	Metric	English	Comments
Haze	8.0 % @Thickness 0.0250 mm	8.0 % @Thickness 0.000984 in	ASTM D1003
Gloss	54 %	54 %	45°; 1 mil; ASTM D1894

Processing Properties	Metric	English	Comments
Melt Temperature	220 - 230 °C	428 - 446 °F