| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM AR9100 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.9 g/10 min @Load 6.60 kg, Temperature 337 °C |
6.9 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17300 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.34 GPa | 629 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 193 MPa | 28000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 5.03 GPa | 730 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| 4.80 J/cm @Thickness 3.20 mm |
8.99 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C @Thickness 6.40 mm |
405 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FAA Flammability, FAR 25.853 A/B | NATURAL | FAR 25.853 |
| NBS Smoke Density, Flaming, Dmax | 5 | ASTM E 662 |
| NBS Smoke Density, Flaming, Ds 1.5 min | 0 | ASTM E 662 |
| NBS Smoke Density, Flaming, Ds 4 min | 5 | ASTM E 662 |
| OSU total heat release (2 minute test) | 5kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 40kW/m^2 | FAR 25.853 |
| Vertical Burn a (60s) passes at | 0sec | FAR 25.853 |
| Vertical Burn b (12s) passes at | 0sec | FAR 25.853 |
Users viewing this material also viewed the following:
- MV Labs YB810 Yb2O3 Ytterbium oxide
- NCMT NanoPAC™ HS403 High Performance Polypropylene Nanocomposite
- Kraton® Cariflex™ IR0310 K Polyisoprene
- Borealis Bormed™ RB845MO Random Copolymer for Healthcare Applications
- Chase Plastics CP Pryme® N130GL (DAM) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated
- Hexcel® HexWeb® HRH-10 - 3/16 - 3.0 Aramid Fiber/Phenolic Resin Honeycomb
- 3M 7680-S Cold Shrink QT-III Silicone Rubber Skirted Termination Kits
- 3M Scotchlite™ 680-72 Reflective Graphic Film
- Arlon 55949C028 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved