SABIC Innovative Plastics LNP THERMOCOMP 5E003M FP-V (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 5E003M FP-V (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 5E003M is a compound based on PVDF resin containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | ASTM D792 |
| Density | 1.76 g/cc | 0.0636 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
| 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.1 % | 6.1 % | 5 mm/min; ISO 527 |
| 6.8 % | 6.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.4 % | 3.4 % | 5 mm/min; ISO 527 |
| 3.5 % | 3.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 7.45 GPa | 1080 ksi | 1 mm/min; ISO 527 |
| 9.06 GPa | 1310 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 79.0 MPa | 11500 psi | ISO 178 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.47 GPa | 793 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.58 GPa | 954 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.32 J/cm | 8.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 92.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
51.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 885 (FG) Synthetic Oil
- Polimeri Europa Edistir N 1782 Polystyrene
- SABIC Innovative Plastics Cycoloy® RCM6134 PC+ABS (Asia Pacific)
- Huntsman Araldite GT 6084 Bisphenol A Epoxy Solid Resin
- Silikony Polskie Gumosil AD-1 A/B Silicone Rubber
- Vyncolit BXE650 Inorganic Filled Phenolic Molding Compound
- ConocoPhillips ANDEROL® 783-1 Series Synthetic Food Grade Greases, NLGI Grade 1
- Cotronics Duralco™ 120 500°F Silver Filled Epoxy, Electrically Conductive
- DuPont Performance Polymers VTR 8605 (GF-S), VTR 8600 (GF-S) 8605/VTR 8600 Blend (discontinued **)
Copyright © lookpolymers.com All Rights Reserved