- Polykemi AB POLYelast TPE ZC100 D40 Thermoplastic Elastomer
Polykemi AB POLYelast TPE ZC100 D40 Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE ZC100 D40 Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | With Flow; ISO 2577 |
| 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 56 @Time 15.0 sec |
56 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
| Elongation at Yield | 16 % | 16 % | ISO/R527 |
| Flexural Strength | <= 26.0 MPa | <= 3770 psi | ISO 178 |
| Flexural Modulus | 0.670 GPa @Temperature 23.0 °C |
97.2 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 55.0 °C @Load 5.001 kg |
131 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 110 °C @Load 1.00 kg |
230 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | |
| Mold Temperature | 20.0 - 60.0 °C | 68.0 - 140 °F | |
| Injection Pressure | 90.0 - 110 MPa | 13100 - 16000 psi | |
| Back Pressure | 0.200 - 0.500 MPa | 29.0 - 72.5 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Niche Polymer PCABSN10BK PC/ABS
- Polykemi AB SCANBLEND P AP2060 F30 PBT/ASA, Glass Fiber Reinforced
- Solvay Engineered Polymers SEQUEL® 1718HFLS Engineered Polyolefin (discontinued **)
- Nitriflex N-8 NBR - Nitrile Rubber
- M. Holland Company PP710 Polypropylene Homopolymer
- Solvay TECHNYL® B 50 H1 PA66/6, DRY
- Teknor Apex Sinpolene MBW2442 Low Density Polyethylene
- Tra-Con Tra-Bond 716K02 Thixotropic Adhesive
- Eagle Brass 519 Phosphor Bronzes 6%, Spring
- Colorite Polymers 4014-Foam General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved