Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.35 %
0.35 %
Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ISO 294-4
Melt Flow 25.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 25.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Calculated from Volume Flow Rate of 21 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 70
70
ISO 2039-2
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
ISO 527-1/-2
Elongation at Yield 6.0 %
6.0 %
ISO 527-1/-2
Tensile Modulus 2.20 GPa
319 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.30 GPa
334 ksi
ISO 178
Izod Impact, Notched (ISO) 40.0 kJ/m²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/4A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature 20.0 °C
 36.1 µin/in-°F

@Temperature 68.0 °F
 ISO 11359-1/-2
Maximum Service Temperature, Air 125 °C
257 °F
Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
ISO 75-1/-2
Vicat Softening Point 135 °C
275 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
 IEC 60695-11-10
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 IEC 60695-11-10
Oxygen Index 35 %
35 %
ISO 4589-1/-2
Glow Wire Test 960 °C

@Thickness 1.50 mm
 1760 °F

@Thickness 0.0591 in
 Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 2.8

@Frequency 1e+6 Hz
 2.8

@Frequency 1e+6 Hz
 IEC 60250
2.9

@Frequency 100 Hz
 2.9

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 29.0 kV/mm
737 kV/in
IEC 60243-1
Dissipation Factor 0.00066

@Frequency 100 Hz
 0.00066

@Frequency 100 Hz
 IEC 60250
0.0092

@Frequency 1e+6 Hz
 0.0092

@Frequency 1e+6 Hz
 IEC 60250
Comparative Tracking Index 250 - 399 V
250 - 399 V
PLC 2; UL 746A
Descriptive Properties Value Comments
Flame Retardant Yes
Flame Retarding Agent Yes
Heat stabilized or stable to heat Yes
High impact or impact modified Yes
Injection molding Yes
Platable Yes
Release Agent Yes
Thermoforming Yes
Without Fillers Yes