Mitsubishi XantarÂ® FC 23 R Polycarbonate

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer	Mitsubishi
Trade Name	Xantar®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Mitsubishi XantarÂ® FC 23 R Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

XantarÂ® materials are engineered for performance, consistency and reliability. This makes XantarÂ® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The XantarÂ® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the XantarÂ® product line from DSM in 2010.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/inÂ³	ISO 1183
Water Absorption	0.35 %	0.35 %	Sim. to ISO 62
Viscosity Test	52 cmÂ³/g	52 cmÂ³/g	Limiting Viscosity Number; ISO 1628-4
	58 cmÂ³/g	58 cmÂ³/g	Viscosity Number
Linear Mold Shrinkage, Flow	0.0060 cm/cm	0.0060 in/in	ISO 294-4
Melt Flow	8.4 g/10 min @Load 1.20 kg, Temperature 300 Â°C	8.4 g/10 min @Load 2.65 lb, Temperature 572 Â°F	Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	70	70	ISO 2039-2
Tensile Strength, Yield	60.0 MPa	8700 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	ISO 527-1/-2
Tensile Modulus	2.30 GPa	334 ksi	ISO 527-1/-2
Flexural Strength	90.0 MPa	13100 psi	ISO 178
Flexural Modulus	2.40 GPa	348 ksi	ISO 178
Izod Impact, Notched (ISO)	80.0 kJ/mÂ² @Temperature 23.0 Â°C	38.1 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 180/4A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	65.0 Âµm/m-Â°C @Temperature 20.0 Â°C	36.1 Âµin/in-Â°F @Temperature 68.0 Â°F	ISO 11359-1/-2
Maximum Service Temperature, Air	125 Â°C	257 Â°F	Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	130 Â°C	266 Â°F	ISO 75-1/-2
Vicat Softening Point	148 Â°C	298 Â°F	50Â°C/h 50N; ISO 306
UL RTI, Electrical	130 Â°C @Thickness 1.50 mm	266 Â°F @Thickness 0.0591 in	UL746B
	130 Â°C @Thickness 3.00 mm	266 Â°F @Thickness 0.118 in	UL746B
UL RTI, Mechanical with Impact	125 Â°C @Thickness 1.50 mm	257 Â°F @Thickness 0.0591 in	UL746B
	125 Â°C @Thickness 3.00 mm	257 Â°F @Thickness 0.118 in	UL746B
UL RTI, Mechanical without Impact	125 Â°C @Thickness 1.50 mm	257 Â°F @Thickness 0.0591 in	UL746B
	130 Â°C @Thickness 3.00 mm	266 Â°F @Thickness 0.118 in	UL746B
Flammability, UL94	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	IEC 60695-11-10
	5VA @Thickness 3.00 mm	5VA @Thickness 0.118 in	IEC 60695-11-20
Oxygen Index	35 %	35 %	ISO 4589-1/-2
Glow Wire Test	825 Â°C @Thickness 1.50 mm	1520 Â°F @Thickness 0.0591 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	850 Â°C @Thickness 3.00 mm	1560 Â°F @Thickness 0.118 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	960 Â°C @Thickness 3.00 mm	1760 Â°F @Thickness 0.118 in	Glow Wire Flammability Index; IEC 60695-2-12
	960 Â°C @Thickness 1.50 mm	1760 Â°F @Thickness 0.0591 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz	IEC 60250
	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz	IEC 60250
Dielectric Strength	29.0 kV/mm	737 kV/in	IEC 60243-1
Dissipation Factor	0.00066 @Frequency 100 Hz	0.00066 @Frequency 100 Hz	IEC 60250
	0.0092 @Frequency 1e+6 Hz	0.0092 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	225 V	225 V	IEC 60112
	250 - 399 V	250 - 399 V	PLC 2; UL 746A

Descriptive Properties	Value	Comments
Blow Molding	Yes
Flame Retardant	Yes
Flame Retarding Agent	Yes
Heat stabilized or stable to heat	Yes
High impact or impact modified	Yes
Injection molding	Yes
Release Agent	Yes
Without Fillers	Yes