Mitsubishi Xantar® C CM 406 U Polycarbonate/ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Mitsubishi
Trade Name Xantar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Xantar® C CM 406 U Polycarbonate/ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 0.60 %
0.60 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption; Sim. to ISO 62
Melt Flow 27.12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 27.12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 Calculated from Volume Flow Rate of 24 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-1/-2
Tensile Modulus 2.20 GPa
319 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.25 GPa
326 ksi
ISO 178
Izod Impact, Notched (ISO) 35.0 kJ/m²

@Temperature -40.0 °C
 16.7 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/4A
55.0 kJ/m²

@Temperature -20.0 °C
 26.2 ft-lb/in²

@Temperature -4.00 °F
 ISO 180/4A
65.0 kJ/m²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/4A
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ISO 75-1/-2
Vicat Softening Point 120 °C
248 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Glow Wire Test 675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 Glow Wire Flammability Index; IEC 60695-2-12
675 °C

@Thickness 3.00 mm
 1250 °F

@Thickness 0.118 in
 Glow Wire Flammability Index; IEC 60695-2-12
700 °C

@Thickness 1.50 mm
 1290 °F

@Thickness 0.0591 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 2.9

@Frequency 1e+6 Hz
 2.9

@Frequency 1e+6 Hz
 IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Comparative Tracking Index 275 V
275 V
IEC 60112
250 - 399 V
250 - 399 V
PLC 2; UL 746A
Descriptive Properties Value Comments
High impact or impact modified Yes
Injection molding Yes
Light stabilized or stable to light Yes
Release Agent Yes
U.V. stabilized or stable to weather Yes
Without Fillers Yes