Mitsubishi Iupilon® E2000R 5 MFI Polycarbonate With Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Mitsubishi |
| Trade Name | Iupilon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsubishi Iupilon® E2000R 5 MFI Polycarbonate With Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hours at 73°F |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 65 | 65 | ASTM D785 |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 68.5 MPa @Thickness 3.17 mm |
9940 psi @Thickness 0.125 in |
|
| Tensile Strength, Yield | 60.3 MPa @Thickness 3.17 mm |
8750 psi @Thickness 0.125 in |
|
| Elongation at Break | 120 % @Thickness 3.17 mm |
120 % @Thickness 0.125 in |
|
| Flexural Yield Strength | 89.1 MPa @Thickness 3.17 mm |
12900 psi @Thickness 0.125 in |
|
| Flexural Modulus | 2.25 GPa @Thickness 3.17 mm |
326 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 9.77 J/cm @Thickness 3.17 mm |
18.3 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 117 µm/m-°C @Temperature 20.0 °C |
65.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.585 | 1.585 | nD |
| Transmission, Visible | 87 % | 87 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 304 °C | 550 - 580 °F | |
| Middle Barrel Temperature | 299 - 321 °C | 570 - 610 °F | |
| Front Barrel Temperature | 316 - 338 °C | 600 - 640 °F | |
| Nozzle Temperature | 304 - 332 °C | 580 - 630 °F | |
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. |
| Injection Pressure | 110 - 152 MPa | 16000 - 22000 psi | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |
| Clamp Pressure | 27.6 - 68.9 MPa | 4000 - 10000 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed- Edge Gate | Slow to Medium | |
| Injection Speed- Tab Gate | Medium to Fast | |
| Injection Speed- Tunnel Gate | Fast |
Users viewing this material also viewed the following:
- Nye Lubricants 374A (RL) Synthetic Oil
- Dow INSPIRE™ D7030EZ Thermoplastic Polyolefin (discontinued **)
- Dielectric Polymers NT-988-2 Overlap Splice Tape (discontinued **)
- Overview of materials for Polystyrene, Impact Modified
- Ineos ABS Lustran® 743 General Purpose, High-Impact (discontinued **)
- Mar-Bal MB3000-15 Thermoset Polyester Composite Molding Compound
- Dow Corning SE 1896 FR KIT
- ArcelorMittal ZF90 Galvannealed zinc-iron alloy coated steel
- 3M 200 Paper Tape
- DuPont Performance Polymers Kalrez® 3065 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved