Menzolit Menzolit® BMC 2310 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® BMC 2310 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BMC 2310 is a chemically resistant grade reinforced with special fibres. Being completely glass-free (no glass fibre reinforcement) it is specifically recommended for the manufacture of high voltage switchgear where SF6 is used to quench the arc.The specific fibre used is not affected by SF6 gas whereas glass fibre may erode away.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0018 cm/cm | 0.0018 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 20.0 MPa @Temperature 22.0 °C |
2900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 20.0 MPa @Temperature 22.0 °C |
2900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 45.0 MPa @Temperature 22.0 °C |
6530 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 3.50 GPa | 508 ksi | in plane |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.0 µm/m-°C | 6.67 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 165 °C | 329 °F | ISO 11357-2 |
| Oxygen Index | 36 % | 36 % | ISO 4589-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Arc Resistance | >= 185 sec | >= 185 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 150 °C | 275 - 302 °F | Injection moulding, matched metal die |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S80G Silicone Rubber
- LG Chemical HF-350 ABS, High Flow, High Impact
- SolVin 264GC Polyvinyl Chloride General Purpose - Rigid or Plasticized
- Seals Eastern 7027 Butyl and Halobutyl Rubber
- A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy
- Chi Mei Wonderlite® PC-110N Polycarbonate - Flame Retardant
- 3M Scotchkote™ HTX 517 Epoxy HT Lining
- Advanced Polymer Alloys DuraGrip™ DGR 6040 NCHT Thermoplastic Elastomer (TPE)
- PolyOne Synprene® RT-3840E Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved