BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 7423-2 NF3001 is an impact modified, 13% glass reinforced, heat stabilized injection molding PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5mm/min; ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | 5mm/min; ISO 527 |
| 10 % | 10 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 5.10 GPa | 740 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM Test |
| Flexural Modulus | 3.66 GPa | 531 ksi | ASTM Test |
| 4.70 GPa | 682 ksi | ISO Data | |
| Izod Impact, Notched | 1.23 J/cm @Thickness 3.17 mm |
2.30 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179 |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM Test |
| 256 °C | 493 °F | ISO 75 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM Test |
| 240 °C | 464 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | Yes | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® S-860 Silicone Prepreg, 1581-112NPH E-Glass Reinforced
- Radici Radilon® S RCV3515 (cond.) Nylon 6
- PolyOne Nymax™ GF 1200 A 55 HS Natural Polyamide 66 (Nylon 66)
- Plenco 50125 PET, Pellet, Injection Molded, White (discontinued **)
- Resinlab® CYNERGY CA6307 Adhesive
- Lehmann & Voss LUVOCOM® 80-7705 Polyacetal-copolymer, with carbon fiber, aramid reinforcement and PTFE
- Lubrizol Isoplast® 2531 Engineering Thermoplastic Polyurethane Resin for Medical Applications
- Wellman Wellamid® 22LH-N Unfilled Nylon 66, Lubricated & Heat Stabilized
- Polyram RamShine PAS701 ASA, UV Stabilized
- Entec Hyrene® PS-HI 14/2 High Impact Polystyrene
Copyright © lookpolymers.com All Rights Reserved