Manifattura Cattaneo PA 6.6 30% GF Nylon, Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PA 6.6 30% GF Nylon, Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.7 % @Temperature 23.0 °C |
1.7 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 5.5 % | 5.5 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 76 | 76 | ISO 2039-2 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned 50% RH; ISO 527 |
| 100 MPa | 14500 psi | Dried; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Conditioned 50% RH; ISO 527 |
| 90.0 MPa | 13100 psi | Dried; ISO 527 | |
| Elongation at Break | 5.0 % | 5.0 % | Dried; ISO 527 |
| 12 % | 12 % | Conditioned 50% RH; ISO 527 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | Conditioned 50% RH; ISO 527 |
| 5.90 GPa | 856 ksi | Dried; ISO 527 | |
| Compressive Yield Strength | 28.0 MPa @Strain 1.00 % |
4060 psi @Strain 1.00 % |
ISO 604 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.23 | 0.23 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 3.8 | 3.8 | µm/s. PV = 0.1 MPa-m/s; max P = 28 MPa; MPC Test |
| Limiting Pressure Velocity | 0.330 MPa-m/sec | 9420 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C @Temperature 23.0 - 100 °C |
33.3 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 |
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | IEC 60094 |
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 28.0 kV/mm @Thickness 2.00 mm |
711 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.040 @Frequency 1.00e+6 Hz |
0.040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | No | No |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Ivory | |
| UV Resistance | N | Dried |
| Y | Conditioned 50% RH |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE G 7680 BLK
- Nye Lubricants 855B (FG) Synthetic Oil
- Polymax® Maxelast® P3838 TPE, PP Overmold or Standalone use
- Precision Polymer Engineering Perlast® G50S FFKM White Perfluoroelastomer
- LNP Thermocomp® LF-1003 Polyetheretherketone, Glass Fiber Reinforcement (discontinued **)
- Kraton® G1652 E (SEBS) Linear Triblock Copolymer
- Multibase Multi-Flex® D 4210 TPE Thermoplastic Elastomer
- UBE UBESTA® 3020X25L Rigid Automotive Grade Nylon 12
- Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 2 hr
- Axiall 4520 Flexible PVC
Copyright © lookpolymers.com All Rights Reserved