MRC Polymers NAXALOYâ„¢ 793A7 PC + Polyester Blend
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP |
| Manufacturer | MRC Polymers |
| Trade Name | NAXALOY™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers NAXALOYâ„¢ 793A7 PC + Polyester Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
• Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants can be addedInformation provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D 792 |
| Water Absorption | 0.14 % | 0.14 % | ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D 955 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 275 °C |
18 g/10 min @Load 4.76 lb, Temperature 527 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D 638 |
| Elongation at Break | 50 % | 50 % | ASTM D 638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D 790 |
| Flexural Modulus | 2.136 GPa | 309.8 ksi | ASTM D 790 |
| Izod Impact, Notched | 6.41 J/cm @Temperature 23.0 °C |
12.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ASTM D 648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LGK4010 PC (Asia Pacific)
- LyondellBasell Alathon® H6017 High Density Polyethylene, Injection Molding Grade
- Gromax BFM40-DL04N1 Nylon 6 40% Mineral Filled (Conditioned)
- Karina E 856-08/151-Y-ERYB Beige PVC Compound
- Sinotek Materials B Graphite Roll
- Shinkong Synthetic Fibers Shinite® F102G30 PET, 30% Glass Filled, Fire Retardant, Halogen Free
- A. Schulman POLYBATCH™ U-4444-E Blowing Agent Concentrate Based In PE
- Cytec EN-12 (Conap) Casting, Potting, and Molding Compound
- Chosun Refractories GUN-135L Light-Weight Gunning Castable
Copyright © lookpolymers.com All Rights Reserved