- MRC Polymers NAXALOYâ„¢ 770 GF10 ABS+PC Alloy, 10% Glass Fiber Filled
MRC Polymers NAXALOYâ„¢ 770 GF10 ABS+PC Alloy, 10% Glass Fiber Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | MRC Polymers |
| Trade Name | NAXALOY™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers NAXALOYâ„¢ 770 GF10 ABS+PC Alloy, 10% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Can be UV StabilizedInternal and external lubricant can be addedInformation provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ISO 1183-A |
| Filler Content | 10 % | 10 % | ISO 3451/1-A |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ISO 294 |
| Melt Flow | 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
nominal; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.98 MPa | 10150 psi | ISO 527-1 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 22.8 °C |
5.71 ft-lb/in² @Temperature 73.0 °F |
ISO 180/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 66.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
36.7 µin/in-°F @Temperature -22.0 - 176 °F |
ASTM E831 (TMA) |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 176 °F |
ASTM E831 (TMA) |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 271 °C | 500 - 520 °F | |
| Middle Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Front Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Nozzle Temperature | 260 - 282 °C | 500 - 540 °F | |
| Melt Temperature | 266 - 282 °C | 510 - 540 °F | |
| Mold Temperature | 60.0 - 82.2 °C | 140 - 180 °F | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Dew Point | <= -17.8 °C | <= 0.000 °F | |
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Cushion | 0.330 - 0.635 cm | 0.130 - 0.250 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Moderate | |
| Hold Pressure | 40-60% of injection pressure | |
| Packing Pressure | 50-75% of injection pressure |
Users viewing this material also viewed the following:
- Nabaltec ACTILOX® 200 AS1 AlO(OH) Boehmite
- Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin IM7 12K Carbon Uni-tape
- ExxonMobil LL 3301.34 Premium High Strength Film Resin (discontinued **)
- Indium Corp. Indalloy 135 Tin-Lead Solder Alloy
- SABIC Innovative Plastics LNP LUBRICOMP QCL349 PA 6/10 (Asia Pacific)
- Styrolution PS 486N HIPS
- A. Schulman POLYTROPE™ TPP 504E Extrusion Grade Olefinic Thermoplastic Elastomer
- Unipetrol B High-Conductive Carbon Black Chezacarb
- Beijing Ranger Chem PBT-201-G20 211 Flame Retarding FR PBT
- Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F)
Copyright © lookpolymers.com All Rights Reserved