- Polypropylene with 40% Calcium Carbonate (CaCO3) Filler
- LyondellBasell Hostacomâ„¢ 63A6-4 Polypropylene Homopolymer
LyondellBasell Hostacomâ„¢ 63A6-4 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | LyondellBasell |
| Trade Name | Hostacom™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hostacomâ„¢ 63A6-4 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hostacomâ„¢ 63A6-4 medium high melt flow, 2,200 MPa flexural modulus, 40% calcium carbonate-filled polypropylene homopolymer has an excellent combination of properties, chemical resistance, aesthetics and processability. Uses: lawn and garden equipment, housings, consumer applicationsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D 785 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D 638 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM D 638 |
| Elongation at Break | 90 % | 90 % | ASTM D 638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D 638 |
| Flexural Modulus | 2.20 GPa | 319 ksi | Tangent, 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.368 J/cm | 0.690 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.9 °C | 201 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 221 °C | 430 °F | 0.118 in; UL 746 |
| 221 °C | 430 °F | 0.0590 in; UL 746 | |
| UL RTI, Mechanical with Impact | 221 °C | 430 °F | 0.118 in; UL 746 |
| 221 °C | 430 °F | 0.0590 in; UL 746 | |
| UL RTI, Mechanical without Impact | 221 °C | 430 °F | 0.118 in; UL 746 |
| 221 °C | 430 °F | 0.0590 in; UL 746 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Nye Lubricants 310B (SO) Synthetic Oil
- DuPont Performance Polymers Rynite® FR530L BK507 PET (Unverified Data**)
- SABIC Innovative Plastics Ultem 1010X PEI (Europe-Africa-Middle East)
- Solvay Chemicals Sulphur Hexafluoride electronic grade
- Solvay ANTAROX® BL 330 Surfactant
- Teknor Apex Sarlink® 3445D Thermoplastic Elastomer
- Master Bond EP21TDCHTND Versatile, toughened two component epoxy for bonding, sealing and coating
- 3M Scotchlite™ 680CR-76 Removable Reflective Graphic Film with Comply™ Adhesive
- ExxonMobil Nuto 46 H Series
Copyright © lookpolymers.com All Rights Reserved