- ATI Allegheny Ludlum AL 625HP™ Stainless Steel
ATI Allegheny Ludlum AL 625HP™ Stainless Steel
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | ATI Allegheny Ludlum |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allegheny Ludlum AL 625HP™ Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nickel-based superalloy. Characteristics:exceptional fatigue resistance, excellent resistance to oxidation and corrosion, outstanding strength and toughness over a range of temperatures from cryogenic to 2000°F. Applications: aerospace, chemical processing. Information provided by Allegheny Ludlum
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.44 g/cc | 0.305 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 940 MPa | 136000 psi | |
| Tensile Strength, Yield | 485 MPa | 70300 psi | |
| Elongation at Break | 46 % | 46 % | |
| Modulus of Elasticity | 205 GPa | 29700 ksi | |
| 160 GPa @Temperature 760 °C |
23200 ksi @Temperature 1400 °F |
||
| 170 GPa @Temperature 649 °C |
24700 ksi @Temperature 1200 °F |
||
| 185 GPa @Temperature 427 °C |
26800 ksi @Temperature 801 °F |
||
| 195 GPa @Temperature 204 °C |
28300 ksi @Temperature 399 °F |
||
| Poissons Ratio | 0.306 | 0.306 | |
| 0.31 @Temperature 204 °C |
0.31 @Temperature 399 °F |
||
| 0.316 @Temperature 427 °C |
0.316 @Temperature 801 °F |
||
| 0.324 @Temperature 649 °C |
0.324 @Temperature 1200 °F |
||
| 0.328 @Temperature 760 °C |
0.328 @Temperature 1400 °F |
||
| Shear Modulus | 57.0 GPa @Temperature 871 °C |
8270 ksi @Temperature 1600 °F |
|
| 63.0 GPa @Temperature 649 °C |
9140 ksi @Temperature 1200 °F |
||
| 70.0 GPa @Temperature 427 °C |
10200 ksi @Temperature 801 °F |
||
| 75.0 GPa @Temperature 204 °C |
10900 ksi @Temperature 399 °F |
||
| 79.0 GPa @Temperature 21.0 °C |
11500 ksi @Temperature 69.8 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 93.0 °C |
7.11 µin/in-°F @Temperature 68.0 - 199 °F |
|
| 14.0 µm/m-°C @Temperature 21.0 - 528 °C |
7.78 µin/in-°F @Temperature 69.8 - 982 °F |
||
| 16.2 µm/m-°C @Temperature 21.0 - 927 °C |
9.00 µin/in-°F @Temperature 69.8 - 1700 °F |
||
| Specific Heat Capacity | 0.410 J/g-°C | 0.0980 BTU/lb-°F | |
| Thermal Conductivity | 7.30 W/m-K @Temperature -157 °C |
50.7 BTU-in/hr-ft²-°F @Temperature -251 °F |
|
| 9.20 W/m-K @Temperature -18.0 °C |
63.8 BTU-in/hr-ft²-°F @Temperature -0.400 °F |
||
| 12.6 W/m-K @Temperature 204 °C |
87.4 BTU-in/hr-ft²-°F @Temperature 399 °F |
||
| 15.7 W/m-K @Temperature 427 °C |
109 BTU-in/hr-ft²-°F @Temperature 801 °F |
||
| 19.0 W/m-K @Temperature 649 °C |
132 BTU-in/hr-ft²-°F @Temperature 1200 °F |
||
| 22.8 W/m-K @Temperature 871 °C |
158 BTU-in/hr-ft²-°F @Temperature 1600 °F |
||
| Melting Point | 1280 - 1350 °C | 2340 - 2460 °F | |
| Solidus | 1280 °C | 2340 °F | |
| Liquidus | 1350 °C | 2460 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.40 % | <= 0.40 % | |
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 20 - 23 % | 20 - 23 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Iron, Fe | <= 5.0 % | <= 5.0 % | As Remainder |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Molybdenum, Mo | 8.0 - 10 % | 8.0 - 10 % | |
| Nb + Ta | 3.15 - 4.15 % | 3.15 - 4.15 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Phosphorous, P | <= 0.015 % | <= 0.015 % | |
| Silicon, Si | <= 0.15 % | <= 0.15 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | <= 0.40 % | <= 0.40 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0001289 ohm-cm @Temperature 21.0 °C |
0.0001289 ohm-cm @Temperature 69.8 °F |
|
| 0.0001319 ohm-cm @Temperature 93.0 °C |
0.0001319 ohm-cm @Temperature 199 °F |
||
| 0.0001339 ohm-cm @Temperature 204 °C |
0.0001339 ohm-cm @Temperature 399 °F |
||
| 0.0001359 ohm-cm @Temperature 427 °C |
0.0001359 ohm-cm @Temperature 801 °F |
||
| 0.0001369 ohm-cm @Temperature 760 °C |
0.0001369 ohm-cm @Temperature 1400 °F |
||
| 0.0001379 ohm-cm @Temperature 649 °C |
0.0001379 ohm-cm @Temperature 1200 °F |
||
| Magnetic Permeability | 1.0006 @Temperature 23.9 °C |
1.0006 @Temperature 75.0 °F |
200 Oersted |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Corrosion Rate mils per year | >200 | 10% Hydrochloric Acid, Boiling |
| 0 | Aqua Regia, Ambient | |
| 0 | 20% Formaldehyde, Boiling | |
| 0 | 20% Cupric Chloride, Ambient | |
| 0 | 45% Ferric Chloride, Ambient | |
| 0 | 10% Ammonium Sulfate, Boiling | |
| 1 | 40% Nitric Acid, Boiling | |
| 1.8 | "Green Death Solution", Boiling | |
| 2 | 10% Sulfuric Acid, Boiling |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DL0039E PC (Asia Pacific)
- Quantum PBT
- Struktol TPW 101 Processing Additive
- Zircar Refractory Composites SIL-1 Silica Cloth
- DSM Stanyl® 46HF4130 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Dry)
- ChevronTexaco MCP Grease L NLGI Grade 00
- ChevronTexaco Packers Oil
Copyright © lookpolymers.com All Rights Reserved