LyondellBasell Hifaxâ„¢ RTA3263EUV/1 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ RTA3263EUV/1 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ RTA3263EUV/1 fractional melt flow, 1,700 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent balance of stiffness, impact strength, weather resistance and processability. It was designed primarily for extruded automotive exterior profile applications. Uses: Automotive exterior parts, profilesInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 | 67 | ISO 868 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ISO 527-1, -2 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 1.40 GPa | 203 ksi | Tangent, 0.05 in/min; ASTM D790 |
| 1.70 GPa | 247 ksi | Tangent, 0.5 in/min; ASTM D790 | |
| Gardner Impact | 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| Dart Drop, Total Energy | 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Tear Strength | 160 kN/m | 910 pli | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 63.9 °C | 147 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.9 °C | 111 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.90 % | 0.90 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.10 % @Temperature 121 °C, Time 3600 sec |
1.10 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- RheTech Products RCT120-01 20% Talc Reinforced Polypropylene, Black, Recycled Content
- Oxford Polymers PBT 30GF PBT, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics Lexan® 500RS PC (Europe-Africa-Middle East)
- Pearl Engineering PEPLPET FR-101-H Monofilament Resin
- North Wood Plastics PS with 40% Wood Fiber
- Momentive Performance Materials RTV162 White Adhesive Sealant, Non-Corrosive Paste
- Teknor Apex UNIPRENE® 7100-64 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Orange 10334 Concentrate Based In LLDPE
- Dow Corning SILASTIC® LS 5-8761 FLUOROSILICONE RUBBER BASE
- Schmolz + Bickenbach Thermodur® 2344 EFS Extra Fine Structure - Hot Work Die Steel
Copyright © lookpolymers.com All Rights Reserved