LyondellBasell Hifaxâ„¢ HSBMG265 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ HSBMG265 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ HSBMG265 medium high melt flow, 1,400 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of rigidity, low temperature impact resistance, dimensional stability and processability. It was designed for use in thin-walled bumper fascia applications that require high paint durability. Uses: Automotive exterior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ISO 1183 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | ISO 868 |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527-1, -2 |
| Elongation at Break | 350 % | 350 % | ISO 527-1, -2 |
| Elongation at Yield | 10 % | 10 % | ISO 527-1, -2 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 48.0 kJ/m² @Temperature 23.0 °C |
22.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 64.0 µm/m-°C @Temperature -30.0 - 100 °C |
35.6 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.70 % | 0.70 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 0.900 % @Temperature 121 °C, Time 3600 sec |
0.900 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Nye Lubricants PG-2S Grease
- Renegade Materials Corporation MVK-14 Polyimide FreeForm™ T650-35 8HS Carbon Fabric
- Kolon SPESIN® KP213G15SIBL Glass Fiber Reinforced PBT Compound Resin
- Ineos H38G-02 Polypropylene Homopolymer
- Shakespeare NX-806 Saltwater Nylon Copolymer Fishing Line, 6 lb
- A. Schulman FORMION™ FI 397 Ionomer
- ExxonMobil Oppalyte™ 42AH748 OPP Film
- Fainplast Compounds GK 89/2 Flexible PVC, Flame Retardant Sheathing Lead Free
- Compuestos Dominicanos Polycom CQ-000365 PVC Compound
- Dow Corning XIAMETER® PMCPMEM-1101 Emulsion
Copyright © lookpolymers.com All Rights Reserved