- Wellman Wellamid® FRGS25-6-NBK3 25% Glass Sphere Reinforced Flame Retardant Nylon 66
Wellman Wellamid® FRGS25-6-NBK3 25% Glass Sphere Reinforced Flame Retardant Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® FRGS25-6-NBK3 25% Glass Sphere Reinforced Flame Retardant Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass Sphere Reinforced Flame Retardant Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183-87 |
| Filler Content | 25 % | 25 % | |
| Linear Mold Shrinkage, Flow | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-93 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527-93 |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178-93 |
| Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75-93 |
| Flammability, UL94 | V-0 @Thickness 0.790 mm |
V-0 @Thickness 0.0311 in |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® GSM Nylon, Cast MoS2 Filled Type 6 (ASTM Product Data Sheet)
- ExxonMobil Escorene® LD 722.MV Molding, extrusion and compounding resin (discontinued **)
- Lehmann & Voss LUVOCOM® 20-8261 Polyphthalamide, with carbon fiber, lubricant modified
- Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C
- SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA
- SABIC Innovative Plastics ULTEM XH6050M PEI Copolymer (Asia Pacific)
- Teknor Apex Telcar® TL-2635C Thermoplastic Elastomer
- California Fine Wire NIFE 5200 Nickel Iron Resistance Wire
- Alliance N-35 Neodymium Iron Boron Magnetic Material
- Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched
Copyright © lookpolymers.com All Rights Reserved