- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyurethane, TP
- Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced
- Lubrizol Isoplast® 2540 Engineering Thermoplastic Polyurethane Resin for Medical Applications
Lubrizol Isoplast® 2540 Engineering Thermoplastic Polyurethane Resin for Medical Applications
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Isoplast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Isoplast® 2540 Engineering Thermoplastic Polyurethane Resin for Medical Applications.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | ASTM D638 |
| Tensile Strength, Yield | 190 MPa | 27600 psi | ASTM D638 |
| Elongation at Yield | 190 % | 190 % | ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 310 MPa | 45000 psi | ASTM D638 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D638 |
| Izod Impact, Unnotched | 4.00 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
7.49 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| 4.00 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
7.49 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 17.0 J @Temperature -29.0 °C |
12.5 ft-lb @Temperature -20.2 °F |
ASTM D3763 |
| 31.0 J @Temperature 23.0 °C |
22.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 °C |
7.78 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Unannealed; ASTM D648 |
| 100 °C | 212 °F | Annealed; ASTM D648 | |
| Vicat Softening Point | 186 °C | 367 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 65.0 - 90.0 °C | 149 - 194 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F |
Users viewing this material also viewed the following:
- Westlake EMAC® SP2405 20% Ethylene-Methyl Acrylate Copolymer (discontinued **)
- NOVA Chemicals Dylark® 250P20 High Performance Glass Filled Styrenic
- Lehmann & Voss LUVOCOM® 50/TF/15/BK7284 Polycarbonate, with PTFE, easy flowing
- Mitsui UNISTOLEâ„¢ R-120K Polyolefinic Primer/ Adhesive
- Lucite International Lucite® 41 Acrylic Resin for Casting and Embedments
- Techmer ES HiFill FR® PP CO FR HS
- DuPont Teijin Films Mylar® MC2 Polyester Film, 50 Gauge (14 µm), PVDC Coated
- 3M 9498 Splicing Tape
- Bulk Molding Compounds BMC T60 Grey Wear Resistant Molding Compound
Copyright © lookpolymers.com All Rights Reserved