- Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded
Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Haynes International, Inc. |
| Trade Name | Hastelloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemical process industries.Data provided by the manufacturer, Haynes International, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 9.00 g/cc | 0.325 lb/in³ | at RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 760 MPa | 110000 psi | |
| 265 MPa @Temperature 870 °C |
38400 psi @Temperature 1600 °F |
||
| Tensile Strength, Yield | 525 MPa | 76100 psi | |
| 250 MPa @Temperature 870 °C |
36300 psi @Temperature 1600 °F |
||
| Elongation at Break | 25 % | 25 % | |
| 14 % @Temperature 870 °C |
14 % @Temperature 1600 °F |
||
| Reduction of Area | 22 % | 22 % | |
| 15 % @Temperature 870 °C |
15 % @Temperature 1600 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
||
| 13.5 µm/m-°C @Temperature 20.0 - 700 °C |
7.50 µin/in-°F @Temperature 68.0 - 1290 °F |
||
| 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
||
| 14.8 µm/m-°C @Temperature 20.0 - 900 °C |
8.22 µin/in-°F @Temperature 68.0 - 1650 °F |
||
| 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 5.0 % | 5.0 % | |
| Cobalt, Co | 2.5 % | 2.5 % | |
| Iron, Fe | 6.0 % | 6.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 24 % | 24 % | |
| Nickel, Ni | 63 % | 63 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Vanadium, V | <= 0.60 % | <= 0.60 % |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 1548S (H32GA) Propylene Homopolymer
- PolyOne Geon™ HTX M6307 Polyvinyl Chloride Alloy (PVC Alloy)
- PolyOne Nymax™ 1200 A L Natural Polyamide 66 (Nylon 66)
- SABIC Innovative Plastics Lexan® EXL1112T PC Copolymer (Europe-Africa-Middle East)
- Inno-Comp INNOPOL® CS 1-6140 N 40% Talc-Filled Polypropylene Homopolymer
- LyondellBasell Adflexâ„¢ KS-021P TPO Resin
- Haynes 625 alloy, 20% cold reduction
- SABIC Innovative Plastics LNP THERMOCOMP D551 PC (Asia Pacific)
- Total PPH M3865 Metallocene Isostatic Propylene Polymer, Fiber Grade
- Bulk Molding Compounds BMC 605L Mineral Filled, Glass Fiber Reinforced Polyester Compound
Copyright © lookpolymers.com All Rights Reserved