SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Asia Pacific)

Category Polymer , Thermoplastic , Polyimide, Thermoplastic
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Extem
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Thermoplastic Polyimide Extem* XH1005 Resin.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.60 %

@Time 173000 sec
 0.60 %

@Time 48.0 hour
 ASTM D570
Water Absorption at Saturation 2.3 %
2.3 %
ISO 62
Linear Mold Shrinkage, Flow 0.010 - 0.012 cm/cm

@Thickness 3.20 mm
 0.010 - 0.012 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 6.0 g/10 min

@Load 6.60 kg,
Temperature 367 °C
 6.0 g/10 min

@Load 14.6 lb,
Temperature 693 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 101 MPa
14600 psi
5 mm/min; ISO 527
103 MPa
14900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 6.0 %
6.0 %
5 mm/min; ISO 527
15 %
15 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.16 GPa
458 ksi
1 mm/min; ISO 527
3.42 GPa
496 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 150 MPa
21800 psi
2 mm/min; ISO 178
168 MPa
24400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.85 GPa
413 ksi
2 mm/min; ISO 178
3.13 GPa
454 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.430 J/cm
0.806 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.10 J/cm²
9.99 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 20.0 J

@Temperature 23.0 °C
 14.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 51.0 µm/m-°C

@Temperature 23.0 - 150 °C
 28.3 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 250 °C

@Thickness 3.20 mm
 482 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 225 °C
437 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
235 °C

@Thickness 3.20 mm
 455 °F

@Thickness 0.126 in
 unannealed; ASTM D648
237 °C

@Thickness 6.40 mm
 459 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 252 °C
486 °F
Rate B/50; ISO 306
252 °C
486 °F
Rate B/120; ISO 306
260 °C
500 °F
Rate B/50; ASTM D1525