Lord Adhesives Aeroglaze® M1433 Elastomeric Polyurethane Rain Erosion Coating
| Category | Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Lord Adhesives |
| Trade Name | Aeroglaze® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Aeroglaze® M1433 Elastomeric Polyurethane Rain Erosion Coating.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aeroglaze® M1433 elastomeric coating functions exceptionally well in abrasive environments. Inherent flexibility, corrosion resistance, and energy absorptive properties make Aeroglaze M1433 elastomeric coating highly suitable for protecting radomes, antennae, and leading edges of aircraft. Aeroglaze M1433 elastomeric coating is qualified to Military Specification MIL-C-85322.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.800 g/cc | 0.0289 lb/in³ | M1433B; ASTM D1475-85 |
| 0.980 g/cc | 0.0354 lb/in³ | Mixed; ASTM D1475-85 | |
| 1.04 g/cc | 0.0376 lb/in³ | M1433A; ASTM D1475-85 | |
| Solids Content | 9.0 % | 9.0 % | M1433B; by weight; ASTM D2369-87 Modified |
| 50 % | 50 % | Mixed; by volume; ASTM D2369-87 Modified | |
| 58 % | 58 % | Mixed; by weight; ASTM D2369-87 Modified | |
| 65 % | 65 % | M1433A; by volume; ASTM D2369-87 Modified | |
| 71 % | 71 % | M1433A; by weight; ASTM D2369-87 Modified | |
| Volatile Organic Compounds (VOC) Content | 300 g/l | 300 g/l | M1433A; ASTM D3960-87 |
| 420 g/l | 420 g/l | Mixed; ASTM D3960-87 | |
| 766 g/l | 766 g/l | M1433B; ASTM D3960-87 | |
| Brookfield Viscosity | 0.89 cP @Temperature 25.0 °C |
0.89 cP @Temperature 77.0 °F |
M1433B; typical of water thin materials; ASTM D2196-86; LVT |
| 200 - 600 cP @Temperature 25.0 °C |
200 - 600 cP @Temperature 77.0 °F |
Mixed; ASTM D2196-86; LVT, Spindle #3 @ 30rpm | |
| 700 - 1500 cP @Temperature 25.0 °C |
700 - 1500 cP @Temperature 77.0 °F |
M1433A; ASTM D2196-86; LVT, Spindle #4 @ 30rpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flash Point | 18.9 °C | 66.0 °F | M1433A; Setaflash, Closed Cup; ASTM D3278-82 |
| 43.3 °C | 110 °F | M1433B; Setaflash, Closed Cup; ASTM D3278-82 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 240 - 360 min @Temperature 23.0 °C |
4.00 - 6.00 hour @Temperature 73.4 °F |
|
| Pot Life | 120 min | 120 min | |
| Shelf Life | 6.00 Month @Temperature 15.6 °C |
6.00 Month @Temperature 60.1 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coating Film Dry Weight (gm/ft²/mil) | 2.69 | |
| Mix Ratio | 3.7:1 | by weight |
| 3:1 | by volume |
Users viewing this material also viewed the following:
- LNP Thermocomp® EC-1006 EM Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612 (Unverified Data**)
- Inno-Comp INNOPOL® CS 2-3130 NU UV-Stabilized 30% Talc-Filled Polypropylene Block-Copolymer
- Momentive Performance Materials Siloprenâ„¢ LSR 2742 Liquid Silicone Rubber - Self-Bonding
- Sylvin Technologies 9077-95 LMW Natural PVC for Injection Molding
- Samsung Cheil Industries Starex® VE-0857 ABS, Unreinforced FR
- DuPont Teijin Films Teijin® Tetoron® HSL Polyester Film, 700 Gauge
- Braskem TI2150C High Crystallinity Copolymer Polypropylene
- Arlon 915-10R##-P0 0.015" (0.381 mm) Cured Self-fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved