Lehmann & Voss Nylatron® MR 2007 Polyamide 6, with mineral filler

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Mineral Reinforced, Impact Grade
Manufacturer Lehmann & Voss & Co.
Trade Name Nylatron®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lehmann & Voss Nylatron® MR 2007 Polyamide 6, with mineral filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Low warpage.Isotropic shrinkage characteristics.Information provided by Lehmann & Voss & Co.KG
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
ISO 1183
Linear Mold Shrinkage 0.0060 - 0.012 cm/cm
0.0060 - 0.012 in/in
Mechanical Properties Metric English Comments
Tensile Stress 96.0 MPa
13900 psi
Elongation at Yield 3.2 %
3.2 %
4.2 %
4.2 %
flexural
Modulus of Elasticity 8.30 GPa
1200 ksi
Flexural Strength 150 MPa
21800 psi
Flexural Modulus 7.20 GPa
1040 ksi
Charpy Impact Unnotched 3.60 J/cm²
17.1 ft-lb/in²
edgewise; ISO 179 1eU
Coefficient of Friction, Dynamic 0.40
0.40
Coefficient of Friction, Static 0.35
0.35
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
160 °C
320 °F
short term
Vicat Softening Point 205 °C
401 °F
DIN ISO 306
Processing Properties Metric English Comments
Processing Temperature 270 °C
518 °F
mass temp
Nozzle Temperature 270 - 280 °C
518 - 536 °F
Zone 1 250 - 270 °C
482 - 518 °F
Zone 2 270 - 290 °C
518 - 554 °F
Zone 3 280 - 300 °C
536 - 572 °F
Mold Temperature 70.0 - 110 °C
158 - 230 °F
Drying Temperature 75.0 °C

@Time 36000 - 57600 sec
167 °F

@Time 10.0 - 16.0 hour
Dehumidifying dryer
105 °C

@Time 14400 - 21600 sec
221 °F

@Time 4.00 - 6.00 hour
or
Descriptive Properties Value Comments
Color black