- Lehmann & Voss LUVOCOM® 80/CF/10/BK Polyacetal-copolymer, with carbon fiber
Lehmann & Voss LUVOCOM® 80/CF/10/BK Polyacetal-copolymer, with carbon fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80/CF/10/BK Polyacetal-copolymer, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.No change of electric potential at bearings in case of separation of charge caused by transport and guiding of paper and foil.Bearings, sleeves, control disks, gear wheels, cams.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 70.0 MPa | 10200 psi | |
| Elongation at Yield | 1.2 % | 1.2 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | |
| Flexural Strength | 105 MPa | 15200 psi | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | flatwise; ISO 179 1fU |
| Coefficient of Friction, Dynamic | 0.16 | 0.16 | |
| Coefficient of Friction, Static | 0.12 | 0.12 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Vicat Softening Point | 165 °C | 329 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- M. Holland Company LD505 LDPE (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Asia Pacific)
- SABIC Innovative Plastics Ultem MD131A PEI (Europe-Africa-Middle East)
- Loctite® 3761 Acrylic Light Cure Adhesive
- Buckeye Polymers BP FLEX D5512 RU BLK Thermoplastic Polyolefin
- Plaskolite West Optix® CA - 75 UVT General Purpose Acrylic Resin
- E-Polymers EFLEX® S4060 High Temperature
- Polymer Resources PPX-FR5 Modified PPO, UL 94 V-0 with HDT of 225 F (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved