- HOME
- POLYMER SEARCH
- Thermoplastic
- Acetal (POM)
- Acetal Copolymer, PTFE Filled
- Lehmann & Voss LUVOCOM® 80-7318 Polyacetal-copolymer, with PTFE
Lehmann & Voss LUVOCOM® 80-7318 Polyacetal-copolymer, with PTFE
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-7318 Polyacetal-copolymer, with PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, glide mating with low sliding friction.Bearings, sleeves, control disks, gear wheels, cams.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ISO 1183 |
| Water Absorption | 0.15 % | 0.15 % | 23°C/24h |
| Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 45.0 MPa | 6530 psi | |
| Elongation at Yield | 10 % | 10 % | |
| 13 % | 13 % | flexural | |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | |
| Flexural Strength | 65.0 MPa | 9430 psi | |
| Flexural Modulus | 1.80 GPa | 261 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Reliance Industries Polypropylene Homopolymer
- Braskem PB 601 LDPE Blow Molding Polyethylene (discontinued **)
- SABIC Innovative Plastics Ultem 1010FV PEI
- Solvay Specialty Polymers Algoflon® L105 Polytetrafluoroethylene (PTFE)
- Total PPH 7060 Polypropylene, Homopolymer
- A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET
- Dow Nordel® IP 4725P High Hardness Extruded Profile
- Abatron AboSeal 8104-18 Vinyl-Acrylic-Latex Based Sealant and Caulk
- M. Holland Company MAGMA® LM233-A LLDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved