Lehmann & Voss LUVOCOM® 50-8276 Polycarbonate, with PTFE
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-8276 Polycarbonate, with PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Impact resistance.Body and duty parts in office equipment, gear wheels, grippers, sleeves, sliding elements, switches and plugs.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | |
| Melt Flow | 18.9 g/10 min @Load 1.20 kg, Temperature 300 °C |
18.9 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 50.0 MPa | 7250 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.0 % | 6.0 % | flexural | |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | |
| Flexural Strength | 80.0 MPa | 11600 psi | |
| Flexural Modulus | 1.80 GPa | 261 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | white |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXM123R PC (Asia Pacific)
- Fujipoly Industries Sarcon® XR-j Gap Filler Pad
- LATI Lapex A PES
- Styron CALIBREâ„¢ 200-3 Polycarbonate Resin
- Master Bond EP126 Two Component Toughened Epoxy Adhesive System
- Universal Wire Works C355.0 (AMS 4245) Aluminum Alloy Filler Metal
- A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
- Dow Corning XIAMETER® PMCPPMX-0344 Cyclosiloxane Blend
- Axiall 13840 Coax & Telecom Flexible PVC
- Aremco Ceramacoat™ 845-WHT High Temperature Ceramic-Inorganic Coating
Copyright © lookpolymers.com All Rights Reserved