- HOME
- POLYMER SEARCH
- Thermoplastic
- Polycarbonate (PC)
- Polycarbonate, Carbon Fiber Reinforced
- Lehmann & Voss LUVOCOM® 50-7644 Polycarbonate, with carbon fiber and PTFE
Lehmann & Voss LUVOCOM® 50-7644 Polycarbonate, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-7644 Polycarbonate, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Improved friction and wear behaviour. Emergency running property.High dimensionally stable precision parts.Body and duty parts in office equipment, gear wheels, grippers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 120 MPa | 17400 psi | |
| Elongation at Yield | 1.8 % | 1.8 % | |
| 2.2 % | 2.2 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 165 MPa | 23900 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | slate grey |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ NN-30GF/13T-2S Black Polyamide 66 (Nylon 66)
- Permabond POP Polyolefin Primer
- Michelman® Coating X300™ Plus Water based, moisture and water resistant coating
- Seals Eastern 7204 Ethylene-Propylene Rubber
- Chase Plastics CP Pryme® PC320GR Polycarbonate (Utility Grade), 20% Glass Fiber Reinforced, Mold Release
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=4.5, Diameter 2 mm)
- ExxonMobil Exxsol™ D60 Dearomatized Fluid
- ExxonMobil Mobil DTE Oil 205