Polimeros Mexicanos Rotolene® 93050 Medium Density Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Rotational Molded
Manufacturer	Polimeros Mexicanos
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeros Mexicanos Rotolene® 93050 Medium Density Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Hexene Copolymer Linear Medium Density Polyethylene for rotational molding. This resin is fully UV8 stabilized.Recommended for general purpose applications. Frequently used for water tanks (less than 2000 liters) and small to medium size containers exhibiting very good mechanical properties. When used for inner layers, it provides excellent smooth finish and texture. Natural Polyethylene meets all requirements of US FDA as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Information provided by Polimeros Mexicanos

Physical Properties	Metric	English	Comments
Bulk Density	0.330 - 0.390 g/cc	0.0119 - 0.0141 lb/in³	ASTM D1895
Density	0.935 g/cc	0.0338 lb/in³	ASTM D792
Particle Mesh Size	35 Mesh	35 Mesh	less than 2%; ASTM D1921
ESCR 100% Igepal®	>= 1000 hour	>= 1000 hour	ASTM D1693
ESCR 10% Igepal®	300 hour	300 hour
Melt Flow	5.2 g/10 min @Load 2.16 kg, Temperature 190 °C	5.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	18.6 MPa	2700 psi	50 mm/min; ASTM D638
Elongation at Yield	11.8 %	11.8 %	(2 in/min); ASTM D638
Flexural Modulus	0.689 GPa	100 ksi	1.3 mm/min; ASTM D790B
Impact Test	61.0 J @Temperature -40.0 °C	45.0 ft-lb @Temperature -40.0 °F	0.125 in.; ARM test

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	50.0 °C	122 °F	ASTM D648

Descriptive Properties	Value	Comments
Pourability	2.5 - 4 gr/s
Process	Rotational Molding