Lehmann & Voss LUVOCOM® 19-7912 Polyamide 46, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7912 Polyamide 46, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Antistatic.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 160 MPa | 23200 psi | |
| Elongation at Yield | 3.5 % | 3.5 % | |
| 4.0 % | 4.0 % | flexural | |
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | |
| Flexural Strength | 235 MPa | 34100 psi | |
| Flexural Modulus | 9.00 GPa | 1310 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
| Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® ESD 5500 Static Dissipative Thermoplastic Compound
- PTS Tristar® PC-20GF 20% Glass Reinforced Polycarbonate
- SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+PS
- Hexcel® Redux® 312 Modified epoxy film adhesive (0.015 psf)
- DSM Novamid® 1015G33-8 NAT PA6-GF33
- ACC MM918 Condensation Cure 2-Part Molding Rubber
- 3M ScotchPad™ 818CP Custom Printed Marking Tapes
- Axiall 19881 Wire & Cable Flexible PVC
- Arkema Group KYNAR® 2821-00 Polyvinylidene Fluoride Powder
- Pyrotek Mesh core / Z-6W Tadpoles
Copyright © lookpolymers.com All Rights Reserved