Lehmann & Voss LUVOCOM® 19-7276 Polyamide 46, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7276 Polyamide 46, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 240 MPa | 34800 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 24.0 GPa | 3480 ksi | |
| Flexural Strength | 340 MPa | 49300 psi | |
| Flexural Modulus | 20.0 GPa | 2900 ksi | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | |
| Coefficient of Friction, Static | 0.14 | 0.14 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.0 µm/m-°C | 12.2 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.420 W/m-K | 2.91 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 160 °C | 320 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F | |
| Vicat Softening Point | 290 °C | 554 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1043L Nylon 6/6 (DAM)
- ExxonMobil Escorene® LD 319.92 Film Resin (discontinued **)
- SABIC Innovative Plastics PC2200 PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP ZF0089 PPE+PS
- Tipco Tipcolite® THD 411 Phenolic Compound, Mica, Asbestos & Cellulose, Medium Flow & High Electrical Properties
- UBE UBEPOL VCR617 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Chosun Refractories FAM-1 Flame-Gunning Repair Refractory
- Clariant Renol ABS3460 ABS, General Purpose, Low Gloss
- AK Steel ASTM A 1018, Grade 33 Hot Rolled Carbon Steel, Structural Steel (SS)
Copyright © lookpolymers.com All Rights Reserved