- Acrylonitrile Butadiene Styrene (ABS), Extruded
- Diamond Polymers ABS 3500 EF-Low Gel Extrusion Grade, Low Gel
Diamond Polymers ABS 3500 EF-Low Gel Extrusion Grade, Low Gel
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Diamond Polymers ABS 3500 EF-Low Gel Extrusion Grade, Low Gel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 0.50 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 °C |
0.50 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 °F |
ASTM D1238 |
| 1.8 g/10 min <br>@Load 3.80 kg,<br> Temperature 230 °C |
1.8 g/10 min <br>@Load 8.38 lb,<br> Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 45 % | 45 % | chs 2 in/min; ASTM D638 |
| Elongation at Yield | 2.4 % | 2.4 % | chs 2 in/min; ASTM D638 |
| Flexural Strength | 77.0 MPa <br>@Thickness 3.17 mm |
11200 psi <br>@Thickness 0.125 in |
tangent; chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 2.598 GPa <br>@Thickness 3.17 mm |
376.8 ksi <br>@Thickness 0.125 in |
tangent; chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.282 J/cm <br>@Thickness 3.17 mm,<br> Temperature 23.0 °C |
2.402 ft-lb/in <br>@Thickness 0.125 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 112 °C <br>@Load 1.00 kg,<br> Thickness 3.17 mm |
234 °F <br>@Load 2.20 lb,<br> Thickness 0.125 in |
ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 95 % | 95 % | 60°; ASTM D523 |
Users viewing this material also viewed the following:
- LyondellBasell Montell 16501F8 Butene LLDPE
- I. Stern GPPS-020 General Purpose Crystal Polystyrene
- Inno-Comp INNOPOL® CS 5-8250 W 50% Chalk-Filled High Density Polyethylene
- Lubriplate NO.3V Petroleum-Based Machine Tool Oil
- Unipetrol PE HD LITEN® SB/SL 20 HDPE
- Cossa Polimeri ESTACARB 2060 V0 HF Flame Retardant Polycarbonate
- 3M 7650-S-HSG Cold Shrink QT-III Silicone Rubber Skirted Termination Kits
- BASF Novolen® 2448 L Polypropylene
- ACC EP WQS EPI Engineered Polymers Water Base Quick Set Epoxy
- Bulk Molding Compounds BMC T12-15526 General Purpose Molding Compound
Copyright © lookpolymers.com All Rights Reserved