PolyOne Bergamid™ B70 G45 BK Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ B70 G45 BK Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc @Temperature 23.0 °C |
0.0549 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Linear Mold Shrinkage | 0.00080 - 0.0060 cm/cm @Thickness 4.00 mm, Temperature 23.0 °C |
0.00080 - 0.0060 in/in @Thickness 0.157 in, Temperature 73.4 °F |
Flow Bergmann Method; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 192 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
27800 psi @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
| Elongation at Break | 2.5 % @Thickness 4.00 mm, Temperature 23.0 °C |
2.5 % @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
| Tensile Modulus | 13.0 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
1890 ksi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/1 |
| Flexural Strength | 290 MPa @Temperature 23.0 °C |
42100 psi @Temperature 73.4 °F |
ISO 178 |
| Flexural Modulus | 12.3 GPa @Temperature 23.0 °C |
1780 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 8.70 J/cm² @Temperature 23.0 °C |
41.4 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 0.800 - 3.00 mm |
HB @Thickness 0.0315 - 0.118 in |
ALL; Internal Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Good Dimensional Stability | |
| Good Flow | ||
| Good Stiffness | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 45% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP GRC40 Homopolymer Polypropylene Glass Reinforced
- PolyOne Geon™ Vinyl Fittings M1012 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Momentive Performance Materials TUFELâ„¢ II 94306 Low Volatile Extrusion Heat Cured Rubber
- SABIC Innovative Plastics Xenoy® ENH2900 PBT+PC (Asia Pacific)
- Teknor Apex Sarlink® 3170 Thermoplastic Elastomer
- Diamond Polymers ABSPC 7801 ABS/PC Injection Molding Grade, High Impact, High Heat
- Addiplast Addinyl B2 ZM30 Nylon 6, 30% Mineral Filled
- PolyOne Geon™ Vinyl Wire & Cable W1201 Polyvinyl Chloride, Flexible (PVC, Flexible)
Copyright © lookpolymers.com All Rights Reserved