SABIC Innovative Plastics Valox® 315 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 315 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose polyester. Fully imported product from USA
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.017 - 0.023 cm/cm @Thickness 3.20 mm |
0.017 - 0.023 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 200 % | 200 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 200 µm/m-°C @Temperature -40.0 - 60.0 °C |
111 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Versalloy™ XL 9055X-9 Thermoplastic Elastomer (TPE)
- Qualchem Danamid AFGF-30 Polyamide 66, 30% Glass Fiber
- Polymer Resources TP-FRHG30 Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame Retardant
- Type P-VS-0053 (Union Carbide) Carbon Fiber
- Lanxess Durethan® B 30 S FN30 000000 Nylon 6, Flame Retardant
- A. Schulman PP 3489-01 Polypropylene Homopolymer
- Lubrizol ESTANE® GP70AE Ester Based Thermoplastic Polyurethane (European Grade)
- Arlon R31551R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
- PolyOne Lubri-Tech™ ES-000/15T Polyethersulfone, PTFE Lubricated (discontinued **)
Copyright © lookpolymers.com All Rights Reserved