- Lehmann & Voss LUVOCOM® 1-8064 Polyamide 66, with carbon fiber, lubricant modified, heat stabilized
Lehmann & Voss LUVOCOM® 1-8064 Polyamide 66, with carbon fiber, lubricant modified, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-8064 Polyamide 66, with carbon fiber, lubricant modified, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Antistatic.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 170 MPa | 24700 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.2 % | 3.2 % | flexural | |
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | |
| Flexural Strength | 245 MPa | 35500 psi | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black-grey |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® S3000-S3N Silver-Coated Solid Glass Spheres
- Omya SNOWHITE® 3 - PT Calcium Carbonate
- NIZHNEKAMSKNEFTEKHIM PE 6750H (506H8) High Density Polyethylene
- PolyOne Geon™ Vinyl Wire & Cable WJJC310L Polyvinyl Chloride, Flexible (PVC, Flexible)
- DuPont Performance Polymers Zytel® FG133F1 NC010 Nylon 66 (Unverified Data**)
- Lehmann & Voss LUVOCOM® 1/XCF/25 Polyamide 66, with carbon fiber, heat stabilized
- Shin-Etsu Silicones KSG-830 Fluid
- Unitika A1030JR PA6, Conditioned
- Eastman DuraStar DS2110UVI Polymer, Natural
- Arkema Group Pebax® MX 1059 Polyether Block Amide (PEBA) (Conditioned)