Addiplast Addilene H 490 M20S Flame Retardant Polypropylene, 20% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant , Polypropylene, Mineral Reinforced |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene H 490 M20S Flame Retardant Polypropylene, 20% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, mineral filled, with halogensInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Melt Flow | 12 g/10 min | 12 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 76 | 76 | Conditioned; ISO 868 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned; ISO R 527 |
| Elongation at Break | 12 % | 12 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 2.70 GPa | 392 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | ISO 75-2/AF |
| Vicat Softening Point | 153 °C | 307 °F | ISO 306/A50 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 850 °C | 1560 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Process Technologies Inc Silicone-White Sanitary Gasket
- PolyOne Maxxam® FR PE JR 165 High Density Polyethylene (HDPE) (discontinued **)
- Cookson Group Plaskon® LS-16S Molding Compound (discontinued **)
- Kuraray HYBRAR® PH2 Polypropylene Blend
- Dow Corning LSPBK 20 SILICONE MASTERBATCH BLACK SILICONE
- EMS-Grivory Grivory® XE 4105 black 9992 PA610-GF50
- Colorite Polymers Self Frosting™ 8311SF Vinyl Compound
- 3M 201+ General Use Masking Tape
- 3M FL010009 Lexan Label Product
- 3M Scotch-Weld™ TE015 Polyurethane Reactive Adhesive
Copyright © lookpolymers.com All Rights Reserved