Lavergne VYTEEN PC/ABS 8515 Polycarbonate - Acrylonitrile Butadiene Styrene Alloy

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Lavergne Performance Compounds
Trade Name	VYTEEN
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lavergne VYTEEN PC/ABS 8515 Polycarbonate - Acrylonitrile Butadiene Styrene Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vyteen PC/ABS 8515 is an enhanced PC/ABS alloy with balanced impact/stiffness properties designed for injection molding applications.Features: -High resilience -Excellent processability -High deflection temperatureTypical Applications: -Electronics -Appliances housing -Electrical componentsInformation provided by Bieglo Gmbh for Lavergne Performance Compounds

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/inÂ³	ASTM D792
Linear Mold Shrinkage, Flow	0.0060 - 0.0080 cm/cm	0.0060 - 0.0080 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0070 - 0.0090 cm/cm	0.0070 - 0.0090 in/in	ASTM D955
Melt Flow	10 g/10 min @Load 5.00 kg, Temperature 260 Â°C	10 g/10 min @Load 11.0 lb, Temperature 500 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.0 MPa	7980 psi	50 mm/min; ASTM D638
Flexural Strength	100 MPa	14500 psi	1.3 mm/min; ASTM D790
Flexural Modulus	2.50 GPa	363 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	5.50 J/cm @Temperature 23.0 Â°C	10.3 ft-lb/in @Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	120 Â°C	248 Â°F	ASTM D648

Processing Properties	Metric	English
Feed Temperature	220 - 240 Â°C	428 - 464 Â°F
Middle Barrel Temperature	240 - 260 Â°C	464 - 500 Â°F
Front Barrel Temperature	250 - 270 Â°C	482 - 518 Â°F
Nozzle Temperature	270 - 275 Â°C	518 - 527 Â°F
Melt Temperature	265 - 275 Â°C	509 - 527 Â°F
Mold Temperature	60.0 - 90.0 Â°C	140 - 194 Â°F