DuPont Performance Polymers Crastin® SO653 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SO653 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Bead Filled Polybutylene Terephthalate with Low Warpage CharacteristicsCrastin SO653 NC010 is a 20% glass bead filled polybutylene terephthalate resin for injection molding. It has isotropic properties and low warpage characteristics.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
1.45 g/cc
0.0524 lb/in³
ISO 1183
Water Absorption 0.35 %

@Thickness 2.00 mm
 0.35 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 157000 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 157000 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
193000 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 193000 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
241000 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 241000 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
408000 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 408000 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
530000 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 530000 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
692000 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 692000 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
ISO 527-1/-2
Tensile Stress 5.00 MPa

@Strain 0.160 %,
Time 3600 sec
 725 psi

@Strain 0.160 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
5.00 MPa

@Strain 0.175 %,
Time 36000 sec
 725 psi

@Strain 0.175 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
5.00 MPa

@Strain 0.177 %,
Time 360000 sec
 725 psi

@Strain 0.177 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
5.00 MPa

@Strain 0.210 %,
Time 3.60e+6 sec
 725 psi

@Strain 0.210 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 10 %
10 %
ISO 527-1/-2
Tensile Modulus 3.50 GPa
508 ksi
ISO 527-1/-2
Flexural Strength 90.0 MPa
13100 psi
ISO 178
Shear Modulus 0.120 GPa

@Temperature 160 °C
 17.4 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.191 GPa

@Temperature 120 °C
 27.7 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.419 GPa

@Temperature 70.0 °C
 60.8 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
1.17 GPa

@Temperature 20.0 °C
 170 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.31 GPa

@Temperature -20.0 °C
 190 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.43 GPa

@Temperature -50.0 °C
 207 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Izod Impact, Notched (ISO) 3.50 kJ/m²
1.67 ft-lb/in²
ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²
17.6 ft-lb/in²
ISO 180/1U
34.0 kJ/m²

@Temperature -30.0 °C
 16.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1U
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
5.00 J/cm²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
ISO 179/1eA
0.350 J/cm²

@Temperature -30.0 °C
 1.67 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 2870 MPa

@Pressure 25.0 MPa,
Temperature 23.0 °C
 417000 psi

@Pressure 3630 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
2920 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 423000 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
2970 MPa

@Pressure 15.0 MPa,
Temperature 23.0 °C
 431000 psi

@Pressure 2180 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
3050 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 442000 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
3125 MPa

@Pressure 5.00 MPa,
Temperature 23.0 °C
 453200 psi

@Pressure 725 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
3500 MPa

@Time 3600 sec
 508000 psi

@Time 1.00 hour
 ISO 899-1
Tensile Creep Modulus, 1000 hours 1500 MPa

@Pressure 25.0 MPa,
Temperature 23.0 °C
 217000 psi

@Pressure 3630 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
1640 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 238000 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
1870 MPa

@Pressure 15.0 MPa,
Temperature 23.0 °C
 271000 psi

@Pressure 2180 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
2170 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 315000 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
2380 MPa

@Pressure 5.00 MPa,
Temperature 23.0 °C
 345000 psi

@Pressure 725 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
2400 MPa

@Time 3.60e+6 sec
 348000 psi

@Time 1000 hour
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
Specific Heat Capacity 1.85 J/g-°C
0.442 BTU/lb-°F
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
of melt
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75-1/-2
Vicat Softening Point 195 °C
383 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Flame Spread 24 mm/min

@Thickness 1.00 mm
 0.94 in/min

@Thickness 0.0394 in
 SE/B; ISO 3795 (FMVSS 302)
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 IEC 60250
4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
 0.0090

@Frequency 100 Hz
 IEC 60250
0.016

@Frequency 1.00e+6 Hz
 0.016

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Part Marking Code >PBT-GB20<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America