SABIC Innovative Plastics LNP Thermocomp YF005
| Category | Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp YF005.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* YF005 is a compound based on TPEE resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D 792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.41 % | 0.41 % | 23°C / 50% RH; ISO 62 |
| 0.31 % @Time 86400 sec |
0.31 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 8.3 % | 8.3 % | Type I, 5 mm/min; ASTM D 638 |
| 10.3 % | 10.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 9.5 % | 9.5 % | 5 mm/min; ISO 527 |
| 9.9 % | 9.9 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.36 GPa | 342 ksi | 1 mm/min; ISO 527 |
| 2.37 GPa | 344 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 53.0 MPa | 7690 psi | ISO 178 |
| Flexural Modulus | 1.98 GPa | 287 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.12 GPa | 307 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.31 J/cm @Temperature 23.0 °C |
6.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 9.98 J/cm @Temperature 23.0 °C |
18.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 76.0 kJ/m² @Temperature 23.0 °C |
36.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 177 µm/m-°C @Temperature -30.0 - 30.0 °C |
98.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 186 °C @Thickness 3.20 mm |
367 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced
- Raschig Group PiMC 1253 Highly flame retardant
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Hi-Sil 233 Filler
- Techmer ES Electrafil® DB-50/SS/6/FR Polycarbonate, 6% Stainless Steel Fiber (dry blend), Flame Retardant
- Solvay Specialty Polymers Ryton® V-1 Polyphenylene Sulfide (PPS)
- Solvay RHODAPEX® ESB-70/A2 Surfactant
- Westlake Epolene® E-25 Chemically Modified Polypropylene, Maleation Processed
- DuPont Performance Polymers Zytel® 70G35HSL NC010 Nylon 66 (Unverified Data**)
- Aremco Corr-Paint™ CP4090-S1 High Temperature Protective Coating, Silicone
Copyright © lookpolymers.com All Rights Reserved