- Acrylonitrile Butadiene Styrene (ABS), Molded
- Lavergne VYTEEN ABS 2901 Acrylonitrile Butadiene Styrene
Lavergne VYTEEN ABS 2901 Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYTEEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYTEEN ABS 2901 Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vyteen ABS 2901 is a black recycled general purpose ABS terpolymer with balanced impact/stiffness properties designed for injection molding applications.Features: -Good resilience -Good processability -High stiffnessTypical Applications: -Structural parts -Appliances housing -Electrical components -AutomotiveInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 70.0 MPa | 10200 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.05 J/cm @Temperature 23.0 °C |
1.97 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 160 - 180 °C | 320 - 356 °F | |
| Middle Barrel Temperature | 200 - 210 °C | 392 - 410 °F | |
| Front Barrel Temperature | 210 - 220 °C | 410 - 428 °F | |
| Nozzle Temperature | 210 - 220 °C | 410 - 428 °F | |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |
| Mold Temperature | 50.0 - 60.0 °C | 122 - 140 °F |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND® 592 Conductive Adhesive
- Mitsui Fybrel® E 790 Polyolefin Synthetic Pulp, Wet Processes (discontinued **)
- KKPC KOSYN KSL 342 Styrene-Butadiene Latex
- Haynes Hastelloy® C-22® alloy, all-weld metal, GMAW short arc
- Saint-Gobain Chemlam® 3300 High Mechanical Performance Industrial Laminate
- Zircar Refractory Composites RS-Cloth Refractory Sheet
- Universal Wire Works No. 6 Cobalt Alloy Welding Wire
- Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
- E-Polymers TEKAMID® H12TW Unreinforced Low warpage PA/ABS Alloy
- Arkema Group Pebax® 7233 Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved