Parker Chomerics Tecknit Teckfip™ FIP-E Formed in Place Conductive Elastomer

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Parker Chomerics Tecknit
Trade Name	Teckfip™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Parker Chomerics Tecknit Teckfip™ FIP-E Formed in Place Conductive Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Commercial grade FIP compound designed for moderate shielding performance. The Ag/glass particles are very smooth which leads to very low compression set value. The material is also available as a heat cure compound (HC-FIP-E)Information provided by Chomerics

Physical Properties	Metric	English	Comments
Specific Gravity	1.53 - 2.07 g/cc	1.53 - 2.07 g/cc

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	53 - 75	53 - 75
Tensile Strength	>= 1.88 MPa	>= 273 psi
Elongation at Break	71 %	71 %
Peel Strength	>= 16.75 kN/m	>= 95.58 pli	Typical
Compression Set	30 %	30 %	Recommended
	13 % @Temperature 70.0 °C, Time 79200 sec	13 % @Temperature 158 °F, Time 22.0 hour

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	125 °C	257 °F
Minimum Service Temperature, Air	-55.0 °C	-67.0 °F

Electrical Properties	Metric	English
Volume Resistivity	0.0070 ohm-cm	0.0070 ohm-cm
Surface Resistance	<= 0.012 ohm	<= 0.012 ohm
	<= 0.012 ohm @Temperature 85.0 °C, Time 605000 sec	<= 0.012 ohm @Temperature 185 °F, Time 168 hour

Processing Properties	Metric	English	Comments
Dry Time	>= 0.200 hour	>= 0.200 hour	Tack Free
Cure Time	<= 1440 min	<= 24.0 hour
Shelf Life	1.00 Month	1.00 Month	Syringe
	6.00 Month	6.00 Month	Cartridge

Descriptive Properties	Value	Comments
Color	Ivory
Filler	Silver/Glass Small Particle