- Lavergne VYPET PBT 6300 BK PBT Unreinforced, Impact Modified
Lavergne VYPET PBT 6300 BK PBT Unreinforced, Impact Modified
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Impact Grade , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYPET |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYPET PBT 6300 BK PBT Unreinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vypet PBT 6300 BK is an unreinforced PBT injection molding compound offering excellent dimensional stability, chemical resistance, low moisture absorption and good electrical properties.Features: High surface gloss; Excellent lubricity; Chemical resistant to most oils and greaseTypical Applications: Pumps; Door handle; Tank coversInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 2.00 mm |
0.012 in/in @Thickness 0.0787 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 2.00 mm |
0.015 in/in @Thickness 0.0787 in |
ASTM D955 |
| Ash | 0.00 % | 0.00 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 2.42 GPa | 351 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.660 J/cm @Temperature 23.0 °C |
1.24 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 230 - 250 °C | 446 - 482 °F | |
| Middle Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |
| Front Barrel Temperature | 245 - 260 °C | 473 - 500 °F | |
| Nozzle Temperature | 240 - 255 °C | 464 - 491 °F | |
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi |
Users viewing this material also viewed the following:
- Oxford Polymers OPX782 Polybutylene Terephthalate (PBT), Impact Modified/ Glass Beads
- Nitriflex NP-2021 Powdered Nitrile
- Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Direct Formed (Unverified Data**)
- A. Schulman PP 984 Polypropylene Medium Impact Polypropylene
- Du-Co Ceramics DC-200-L-5 Fosterite
- 3M Nextel™ BF-30 Woven Fabric 440
- 3M GLS100 Glossy Protection Film
- Sylvin Technologies 9604-95 LMW Clear PVC for Injection Molding
- Bhansali Engineering Abstron IMC-45 ABS-PC Alloy
Copyright © lookpolymers.com All Rights Reserved