ExxonMobil LL 3002.32 Cast Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 3002.32 Cast Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LL 3002.32 is a hexene copolymer LLDPE cast film resin. Films produced from this resin have excellent tensile properties, as well as stiffness and toughness. Combined with good drawdown properties, LL 3002.32 resin is a versatile packaging film resin.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ExxonMobil Method
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.93 MPa
1150 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 7.38 MPa
1070 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 440 %
440 %
ASTM D882
Film Elongation at Break, TD 840 %
840 %
ASTM D882
Puncture Energy 3.28 J
2.42 ft-lb
ExxonMobil
Elmendorf Tear Strength, MD 11.32 g/micron
287.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 36.91 g/micron
937.5 g/mil
ASTM D1922
Dart Drop 3.94 g/micron
100 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 64.0 MPa
9280 psi
ASTM D882
Film Tensile Strength at Break, TD 41.2 MPa
5980 psi
ASTM D882
1% Secant Modulus, MD 110 MPa
15900 psi
ASTM D882
1% Secant Modulus, TD 123 MPa
17900 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 109 °C
228 °F
ASTM D3418
Optical Properties Metric English Comments
Haze 1.6 %
1.6 %
ASTM D1003
Gloss 91 %
91 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer
Copyright © lookpolymers.com All Rights Reserved