Samsung Cheil Industries Starex® SF-0950S MABS, Unreinforced Scratch Resistant

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® SF-0950S MABS, Unreinforced Scratch Resistant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 13 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 13 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength, Yield 42.2 MPa
6120 psi
5 mm/min; ASTM D638
Flexural Strength 63.7 MPa
9240 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.06 GPa
299 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.08 J/cm

@Thickness 3.17 mm
 2.02 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 92.0 °C
198 °F
B/50; ISO R306
Flammability, UL94 HB

@Thickness 1.50 - 3.00 mm
 HB

@Thickness 0.0591 - 0.118 in
Descriptive Properties Value Comments
Pencil Hardness H
500g, JIS K 5401