SABIC Innovative Plastics LNP THERMOCOMP LF008 PEEK (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LF008 PEEK (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* LF008 is a compound based on Polyetheretherketone resin containing Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 |
| 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 154 MPa | 22300 psi | ASTM D638 |
| 155 MPa | 22500 psi | ISO 527 | |
| Tensile Strength, Yield | 156 MPa | 22600 psi | ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.4 % | 2.4 % | ISO 527 | |
| Elongation at Yield | 2.2 % | 2.2 % | ISO 527 |
| 2.4 % | 2.4 % | ASTM D638 | |
| Tensile Modulus | 12.81 GPa | 1858 ksi | 1 mm/min; ISO 527 |
| 13.78 GPa | 1999 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 234 MPa | 33900 psi | ASTM D790 |
| 240 MPa | 34800 psi | ISO 178 | |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| 10.4 GPa | 1510 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.11 J/cm | 15.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 3.60 µm/m-°C @Temperature -40.0 - 40.0 °C |
2.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 4.00 µm/m-°C @Temperature -40.0 - 40.0 °C |
2.22 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 1.80 µm/m-°C @Temperature -40.0 - 40.0 °C |
1.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 2.00 µm/m-°C @Temperature -40.0 - 40.0 °C |
1.11 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200H-10 Fiberglass Reinforced Thermoset SMC
- PTS Tristar® PC-10R-(V20) 20 MFI UV Stabilized Polycarbonate with Release
- Hong Kun Group 2,6-Diacetylpyridine Pharmaceutical Intermediate
- Momentive Performance Materials Siloprenâ„¢ LSR 2030 Liquid Silicone Rubber - General Purpose
- Isoflon PTFE +28% GL Blue-E glass-1% Blue Polytetrafluoroethylene with 28% GL-Blue-E glass-1% Blue (equivalent VX1)
- Dyna-Purge® B Purging Compound
- Shin-Etsu Silicones KE-9611U Silicone Elastomer
- Polyplastics Duranex® 2000 Polybutylene Terephthalate (PBT), High flow
- DuPont Elvanol® 51-03 Polyvinyl Alcohol Partially Hydrolyzed General Purpose Grade
- 3M 7902 Screen Printable Sheet Vinyl Label Material
Copyright © lookpolymers.com All Rights Reserved